1.2mm Thickness Pultruded Carbon Fiber Strip for Structural Strengthening

Basic Info

Model NO.	1.2 T-1
Tensile Strength	> 2800 MPa
Elastic Modulus	>165 Gpa
Elongation at Break	>1.7%
Transport Package	Carton
Specification	1.2MM T-1
Trademark	JLON
Origin	China
HS Code	6815993900
Production Capacity	100000 M2

Product Description

:The T-1/T-2 series carbon fiber plates are pultruded carbon fibre reinforced polymer (CFRP) laminates, designed for strengthening concrete, timber, masonry, steel andfibre reinforced polymer structures.The T-1/T-2 series carbon fiber plates are bonded onto the structureas externally , bonded reinforcement using epoxy resin based adhesive for room temperatures curing.Applications :1.Increased Load Carrying Capacity:Increasing the load capacity of floor slabs, beams and bridge sections▪ For the installation of heavier machinery▪ To stabilise vibrating structures▪ For changes in building use2.Damage to structural elements due to:▪ Deterioration of the original construction materials▪ Steel reinforcement corrosion▪ Accidents (Vehicle impact, earthquakes, fire)3.Improvement of serviceability and durability:▪ Reduced deflection and crack width▪ Stress reduction in the steel reinforcement▪ Improved fatigue resistance4.Change of the structural system:▪ Removal of walls and / or columns▪ Removal of floor and wall sections to create access /openings5.Resistance to possible events:▪Increased resistance to earthquakes, impact or explosion etc.6.To repair design or construction defects such as:▪ Insufficient / inadequate reinforcement▪ Insufficient / inadequate structural depthAdvantages and Benefits:▪ Non-corroding▪ Very high strength▪ Excellent durability and fatigue resistance▪ Unlimited lengths, no joints required▪Low system thickness, simple execution of plate intersections or crossings▪ Easy transportation (rolls)▪Lightweight, very easy to install, especially overhead(without temporary support)▪Minimum preparation of plate, applicable in severallayers▪Smooth edges without exposed fibres as result of production by pultrusion

Typical technical parameters:

Type	T-1	T-2
Nominal Thickness	1.2/1.4 mm	1.2/1.4 mm
Tensile Strength	> 2800 MPa	>2000 MPa
Elastic Modulus	>165 GPa	>140 GPa
Elongation at Break	>1.7%	>1.6%
Width	50/100 mm	50/100 mm